Patterning of nanometer-scale suicide structures on silicon by 'direct writing focus ion-beam implantation'

M. M. Milan, D. P. Pivin, Terry Alford, J. W. Mayer

Research output: Contribution to journalArticle

4 Scopus citations

Abstract

We have developed a new technique for direct patterning and formation of cobalt suicide structures using focused ion beam implantation. This mask-free fabrication technique takes advantage of the influence on the kinetics of ion-beam mixing and properties of thin barrier oxides during suicide line formation. Suicide structures with dimensions of the order of 170 nm were produced on (100) silicon substrates. The process involves the ion implantation of 200 keV As+ + through a thin cobalt film on SiO2/Si structure. A selective reaction barrier at the Si/Co interface comprising of a thin (∼ 2 nm) oxide (SiO2), prevents unwanted reactions with silicon. Ion-beam mixing was instrumental in fracturing of the oxide layer, thereby allowing the migration of metal atoms across the Si/Co boundary for the silicidation reaction to proceed during subsequent rapid thermal anneal treatments. Diffusion controlled reactions advanced rapidly in the implanted areas, requiring a two-step anneal sequence to inhibit reaction elsewhere. A threshold dose of 3 × 1015 cm-2 was required for process initiation. Four-terminal resistance test structures were formed for electrical measurements. Resistivity obtained ranged on the order of 12 to 23 μΩ-cm. Application of this method can facilitate a wide variety of suicide structures.

Original languageEnglish (US)
Pages (from-to)219-224
Number of pages6
JournalThin Solid Films
Volume411
Issue number2
DOIs
StatePublished - Dec 1 2002

Keywords

  • Cobalt
  • Ion beam
  • Patterning
  • Suicides

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Patterning of nanometer-scale suicide structures on silicon by 'direct writing focus ion-beam implantation''. Together they form a unique fingerprint.

  • Cite this