Observation of heavy- and light-hole split direct bandgap photoluminescence from tensile-strained GeSn (0.03% Sn)

Thomas R. Harris, Yung Kee Yeo, Mee Yi Ryu, Richard T. Beeler, John Kouvetakis

Research output: Contribution to journalArticle

15 Scopus citations

Abstract

Temperature- (T-) and laser power-dependent photoluminescence (PL) measurements have been made for the tensile-strained, undoped GeSn (0.03% Sn) film grown on Si substrate. The PL results show not only clear strain-split direct bandgap transitions to the light-hole (LH) and heavy-hole (HH) bands at energies of 0.827 and 0.851 eV at 10 K, respectively, but also clearly show both strong direct and indirect bandgap related PL emissions at almost all temperatures, which are rarely observed. This split of PL emissions can be directly observed only at low T and moderate laser power, and the two PL peaks merge into one broad PL peak at room temperature, which is mainly due to the HH PL emission rather than LH transition. The evolution of T-dependent PL results also clearly show the competitive nature between the direct and indirect bandgap related PL transitions as T changes. The PL analysis also indicates that the energy gap reduction in Γ valley could be larger, whereas the bandgap reduction in L valley could be smaller than the theory predicted. As a result, the separation energy between Γ and L valleys (∼86 meV at 300 K) is smaller than theory predicted (125 meV) for this Ge-like sample, which is mainly due to the tensile strain. This finding strongly suggests that the indirect-to-direct bandgap transition of Ge1-ySny could be achieved at much lower Sn concentration than originally anticipated if one utilizes the tensile strain properly. Thus, Ge1-ySny alloys could be attractive materials for the fabrication of direct bandgap Si-based light emitting devices.

Original languageEnglish (US)
Article number103502
JournalJournal of Applied Physics
Volume116
Issue number10
DOIs
StatePublished - Sep 14 2014

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Observation of heavy- and light-hole split direct bandgap photoluminescence from tensile-strained GeSn (0.03% Sn)'. Together they form a unique fingerprint.

  • Cite this