In situ structure characterization of airborne carbon nanofibres by a tandem mobility-mass analysis

Bon Ki Ku, Mark S. Emery, Andrew D. Maynard, Mark R. Stolzenburg, Peter H. McMurry

Research output: Contribution to journalArticle

59 Scopus citations

Abstract

Carbon nanofibres aerosolized by the agitation of as-produced commercial powder have been characterized in situ by using the differential mobility analyser-aerosol particle mass analyser (DMA-APM) method to determine their structural properties such as the effective density and fractal dimension for toxicology study. The effective density of the aerosolized carbon nanofibres decreased from 1.2 to 0.4 g cm-3 as the mobility diameters increased from 100 to 700 nm, indicating that the carbon nanofibres had open structures with an overall void that increased with increasing diameter, due to increased agglomeration of the nanofibres. This was confirmed by transmission electron microscopy (TEM) observation, showing that 100 nm mobility diameter nanofibres were predominantly single fibres, while doubly or triply attached fibres were seen at mobility diameters of 200 and 400 nm. Effective densities calculated using Cox's theory were in reasonable agreement with experimental values. The mass fractal dimension of the carbon nanofibres was found to be 2.38 over the size range measured and higher than that of single-walled carbon nanotubes (SWCNTs), suggesting that the carbon nanofibres have more compact structure than SWCNTs.

Original languageEnglish (US)
Article number042
Pages (from-to)3613-3621
Number of pages9
JournalNanotechnology
Volume17
Issue number14
DOIs
StatePublished - Jul 28 2006
Externally publishedYes

ASJC Scopus subject areas

  • Bioengineering
  • Chemistry(all)
  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'In situ structure characterization of airborne carbon nanofibres by a tandem mobility-mass analysis'. Together they form a unique fingerprint.

  • Cite this