Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite

Masoud Yekani Fard, Brian Raji, Evi Postelnicu, Xiao Cheng, Seid Mohamadali Sadat, Aditi Chattopadhyay

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

Fracture mechanic behavior of a type of stitch-bonded biaxial carbon epoxy composite is presented. The influence of damage modes such as separation, tow splitting, multiple cracks, and fiber bridging on the energy release rate initiation and resistance of thin and thick laminates is investigated. The possible effects of manufacturing and in-service environmental conditions on energy release rate initiation and propagation have been presented. Details of loading speed, crack velocity, plasticity zone, curing and environmental conditions for smooth and nonsmooth crack growth have been discussed. The curing and in-service conditions have been found to influence the mode I fracture behavior of composite laminates. The results showed that different propagation curves should be included in the design guidelines for stitch-bonded composites.

Original languageEnglish (US)
Title of host publicationCollection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference
StatePublished - 2013
Event54th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference - Boston, MA, United States
Duration: Apr 8 2013Apr 11 2013

Other

Other54th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference
CountryUnited States
CityBoston, MA
Period4/8/134/11/13

Fingerprint

Curing
Carbon
Energy release rate
Laminates
Composite materials
Cracks
Fracture mechanics
Temperature
Plasticity
Crack propagation
Fibers

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Materials Science(all)
  • Aerospace Engineering
  • Architecture

Cite this

Yekani Fard, M., Raji, B., Postelnicu, E., Cheng, X., Sadat, S. M., & Chattopadhyay, A. (2013). Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite. In Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference [AIAA 2013-1907]

Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite. / Yekani Fard, Masoud; Raji, Brian; Postelnicu, Evi; Cheng, Xiao; Sadat, Seid Mohamadali; Chattopadhyay, Aditi.

Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference. 2013. AIAA 2013-1907.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Yekani Fard, M, Raji, B, Postelnicu, E, Cheng, X, Sadat, SM & Chattopadhyay, A 2013, Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite. in Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference., AIAA 2013-1907, 54th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference, Boston, MA, United States, 4/8/13.
Yekani Fard M, Raji B, Postelnicu E, Cheng X, Sadat SM, Chattopadhyay A. Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite. In Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference. 2013. AIAA 2013-1907
Yekani Fard, Masoud ; Raji, Brian ; Postelnicu, Evi ; Cheng, Xiao ; Sadat, Seid Mohamadali ; Chattopadhyay, Aditi. / Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite. Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference. 2013.
@inproceedings{f360fb864b0a48b8b82b137cf5e63cc4,
title = "Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite",
abstract = "Fracture mechanic behavior of a type of stitch-bonded biaxial carbon epoxy composite is presented. The influence of damage modes such as separation, tow splitting, multiple cracks, and fiber bridging on the energy release rate initiation and resistance of thin and thick laminates is investigated. The possible effects of manufacturing and in-service environmental conditions on energy release rate initiation and propagation have been presented. Details of loading speed, crack velocity, plasticity zone, curing and environmental conditions for smooth and nonsmooth crack growth have been discussed. The curing and in-service conditions have been found to influence the mode I fracture behavior of composite laminates. The results showed that different propagation curves should be included in the design guidelines for stitch-bonded composites.",
author = "{Yekani Fard}, Masoud and Brian Raji and Evi Postelnicu and Xiao Cheng and Sadat, {Seid Mohamadali} and Aditi Chattopadhyay",
year = "2013",
language = "English (US)",
isbn = "9781624102233",
booktitle = "Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference",

}

TY - GEN

T1 - Effects of curing temperature and environmental conditions on mode i fracture behavior for a laminated biaxial carbon/epoxy composite

AU - Yekani Fard, Masoud

AU - Raji, Brian

AU - Postelnicu, Evi

AU - Cheng, Xiao

AU - Sadat, Seid Mohamadali

AU - Chattopadhyay, Aditi

PY - 2013

Y1 - 2013

N2 - Fracture mechanic behavior of a type of stitch-bonded biaxial carbon epoxy composite is presented. The influence of damage modes such as separation, tow splitting, multiple cracks, and fiber bridging on the energy release rate initiation and resistance of thin and thick laminates is investigated. The possible effects of manufacturing and in-service environmental conditions on energy release rate initiation and propagation have been presented. Details of loading speed, crack velocity, plasticity zone, curing and environmental conditions for smooth and nonsmooth crack growth have been discussed. The curing and in-service conditions have been found to influence the mode I fracture behavior of composite laminates. The results showed that different propagation curves should be included in the design guidelines for stitch-bonded composites.

AB - Fracture mechanic behavior of a type of stitch-bonded biaxial carbon epoxy composite is presented. The influence of damage modes such as separation, tow splitting, multiple cracks, and fiber bridging on the energy release rate initiation and resistance of thin and thick laminates is investigated. The possible effects of manufacturing and in-service environmental conditions on energy release rate initiation and propagation have been presented. Details of loading speed, crack velocity, plasticity zone, curing and environmental conditions for smooth and nonsmooth crack growth have been discussed. The curing and in-service conditions have been found to influence the mode I fracture behavior of composite laminates. The results showed that different propagation curves should be included in the design guidelines for stitch-bonded composites.

UR - http://www.scopus.com/inward/record.url?scp=84881328162&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84881328162&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:84881328162

SN - 9781624102233

BT - Collection of Technical Papers - AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference

ER -