Defects in single-crystal silicon induced by hydrogenation

N. M.P. Johnson, F. A. Ponce, R. A. Street, R. J. Nemanich

Research output: Contribution to journalArticle

408 Scopus citations

Abstract

It is demonstrated that hydrogenation induces microdefects and electronic deep levels in single-crystal silicon, which are unrelated to either plasma or radiation damage. After hydrogenation of either n-type or p-type silicon, transmission electron microscopy reveals defects that can be described as hydrogen-stabilized platelets or microcracks which appear within 0.1 1/4m of the exposed surface and are predominantly oriented along {111} crystallographic planes. These defects correlate with high concentrations of hydrogen or deuterium as measured by secondary-ion mass spectrometry and with the appearance of SiH bonds as revealed by Raman spectroscopy. The concomitant introduction of electrically active gap states is demonstrated with both photoluminescence spectroscopy (PL) and deep-level transient spectroscopy (DLTS). In PL several H-induced radiative transitions are observed, with the dominant peak at 0.98 eV, which had previously been ascribed to plasma damage. In n-type Schottky diodes, DLTS detects two H-induced levels with thermal activation energies for electron emission of approximately 0.06 and 0.51 eV. These defects are detected at depths greater than the surface layer, are in low concentrations (<1013 cm-3), are acceptorlike, and anneal with an activation energy of 1/40.3 eV.

Original languageEnglish (US)
Pages (from-to)4166-4169
Number of pages4
JournalPhysical Review B
Volume35
Issue number8
DOIs
StatePublished - Jan 1 1987
Externally publishedYes

ASJC Scopus subject areas

  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Defects in single-crystal silicon induced by hydrogenation'. Together they form a unique fingerprint.

  • Cite this