Corrosion-induced flexural behavior degradation of locally ungrouted post-tensioned concrete beams

Xuhui Zhang, Lei Wang, Jianren Zhang, Yongming Liu

Research output: Contribution to journalArticle

9 Citations (Scopus)

Abstract

Strand corrosion within the insufficient grouted duct has become a serious problem affecting the durability of bridge structures. The residual flexural behavior of the locally ungrouted post-tensioned concrete beams after strand corrosion is investigated in the present study. Two experiments are performed: corroded strand test for the constitutive law development and beam test for the flexural behavior investigation. An analytical model is proposed to predict the ultimate strength, the deformation, and the strain response of corroded beams under external loadings. The proposed model considers the strain compatibility between strand and concrete, material mechanics deterioration of strand, and the asymmetric deflection due to local corrosion in ungrouted duct. The accuracy of the model is verified by the experimental observations. Results show that corrosion loss has less effect on the yield strength and elastic modulus than that on the ultimate strain of strand. It is also observed that light corrosion has little effect on the beam cracking and the load-deflection behavior before beam cracking. Severe corrosion degrades significantly the flexural capacity and the local post-cracking stiffness of beams, which leads to the asymmetric deformation and crack formation.

Original languageEnglish (US)
Pages (from-to)7-17
Number of pages11
JournalConstruction and Building Materials
Volume134
DOIs
StatePublished - Mar 1 2017

Fingerprint

Concretes
Corrosion
Degradation
Ducts
Crack initiation
Yield stress
Deterioration
Analytical models
Mechanics
Durability
Elastic moduli
Stiffness
Experiments

Keywords

  • Analytical model
  • Flexural behavior
  • Local grouting
  • PT beam
  • Strand corrosion

ASJC Scopus subject areas

  • Civil and Structural Engineering
  • Building and Construction
  • Materials Science(all)

Cite this

Corrosion-induced flexural behavior degradation of locally ungrouted post-tensioned concrete beams. / Zhang, Xuhui; Wang, Lei; Zhang, Jianren; Liu, Yongming.

In: Construction and Building Materials, Vol. 134, 01.03.2017, p. 7-17.

Research output: Contribution to journalArticle

@article{d6fdfb4b081247b9890699b367c6cd81,
title = "Corrosion-induced flexural behavior degradation of locally ungrouted post-tensioned concrete beams",
abstract = "Strand corrosion within the insufficient grouted duct has become a serious problem affecting the durability of bridge structures. The residual flexural behavior of the locally ungrouted post-tensioned concrete beams after strand corrosion is investigated in the present study. Two experiments are performed: corroded strand test for the constitutive law development and beam test for the flexural behavior investigation. An analytical model is proposed to predict the ultimate strength, the deformation, and the strain response of corroded beams under external loadings. The proposed model considers the strain compatibility between strand and concrete, material mechanics deterioration of strand, and the asymmetric deflection due to local corrosion in ungrouted duct. The accuracy of the model is verified by the experimental observations. Results show that corrosion loss has less effect on the yield strength and elastic modulus than that on the ultimate strain of strand. It is also observed that light corrosion has little effect on the beam cracking and the load-deflection behavior before beam cracking. Severe corrosion degrades significantly the flexural capacity and the local post-cracking stiffness of beams, which leads to the asymmetric deformation and crack formation.",
keywords = "Analytical model, Flexural behavior, Local grouting, PT beam, Strand corrosion",
author = "Xuhui Zhang and Lei Wang and Jianren Zhang and Yongming Liu",
year = "2017",
month = "3",
day = "1",
doi = "10.1016/j.conbuildmat.2016.12.140",
language = "English (US)",
volume = "134",
pages = "7--17",
journal = "Construction and Building Materials",
issn = "0950-0618",
publisher = "Elsevier Limited",

}

TY - JOUR

T1 - Corrosion-induced flexural behavior degradation of locally ungrouted post-tensioned concrete beams

AU - Zhang, Xuhui

AU - Wang, Lei

AU - Zhang, Jianren

AU - Liu, Yongming

PY - 2017/3/1

Y1 - 2017/3/1

N2 - Strand corrosion within the insufficient grouted duct has become a serious problem affecting the durability of bridge structures. The residual flexural behavior of the locally ungrouted post-tensioned concrete beams after strand corrosion is investigated in the present study. Two experiments are performed: corroded strand test for the constitutive law development and beam test for the flexural behavior investigation. An analytical model is proposed to predict the ultimate strength, the deformation, and the strain response of corroded beams under external loadings. The proposed model considers the strain compatibility between strand and concrete, material mechanics deterioration of strand, and the asymmetric deflection due to local corrosion in ungrouted duct. The accuracy of the model is verified by the experimental observations. Results show that corrosion loss has less effect on the yield strength and elastic modulus than that on the ultimate strain of strand. It is also observed that light corrosion has little effect on the beam cracking and the load-deflection behavior before beam cracking. Severe corrosion degrades significantly the flexural capacity and the local post-cracking stiffness of beams, which leads to the asymmetric deformation and crack formation.

AB - Strand corrosion within the insufficient grouted duct has become a serious problem affecting the durability of bridge structures. The residual flexural behavior of the locally ungrouted post-tensioned concrete beams after strand corrosion is investigated in the present study. Two experiments are performed: corroded strand test for the constitutive law development and beam test for the flexural behavior investigation. An analytical model is proposed to predict the ultimate strength, the deformation, and the strain response of corroded beams under external loadings. The proposed model considers the strain compatibility between strand and concrete, material mechanics deterioration of strand, and the asymmetric deflection due to local corrosion in ungrouted duct. The accuracy of the model is verified by the experimental observations. Results show that corrosion loss has less effect on the yield strength and elastic modulus than that on the ultimate strain of strand. It is also observed that light corrosion has little effect on the beam cracking and the load-deflection behavior before beam cracking. Severe corrosion degrades significantly the flexural capacity and the local post-cracking stiffness of beams, which leads to the asymmetric deformation and crack formation.

KW - Analytical model

KW - Flexural behavior

KW - Local grouting

KW - PT beam

KW - Strand corrosion

UR - http://www.scopus.com/inward/record.url?scp=85007367501&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85007367501&partnerID=8YFLogxK

U2 - 10.1016/j.conbuildmat.2016.12.140

DO - 10.1016/j.conbuildmat.2016.12.140

M3 - Article

VL - 134

SP - 7

EP - 17

JO - Construction and Building Materials

JF - Construction and Building Materials

SN - 0950-0618

ER -